Tisan TISESTER® 15% Glass Fiber Reinforced Polybutylene Terephthalate

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer	Tisan Engineering Plastics
Trade Name	TISESTER®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Tisan TISESTER® 15% Glass Fiber Reinforced Polybutylene Terephthalate.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resistanceExcellent toughnessHigh temperature resistanceExcellent chemical resistanceElectrical isolation and arc resistanceHigh performanceEasy processabilityFast cycle time Glass fiber reinforcement imparts high shrinkage resistance and impact resistance to TISESTER products, yielding improvements in thermal features as well. PBT is resistant against solvents, exhibits low shrinkage during shaping, and it is mechanically strong, heat resistant for temperatures up to 150°C, and can be reinforced for flame retardance. Tisester compounds display sufficient resistance against hydrocarbons, alcohols, ethers, acids, and alkali solvents.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0060 cm/cm	0.0060 in/in
Ash	15 %	15 %	ISO 3451

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	82	82	ISO 868
Tensile Strength at Break	115 MPa	16700 psi	ISO 527-2
Tensile Strength, Yield	110 MPa	16000 psi	ISO 527-2
Elongation at Break	3.7 %	3.7 %	ISO 527-2
Elongation at Yield	3.5 %	3.5 %	ISO 527-2
Modulus of Elasticity	5.50 GPa	798 ksi	ISO 527-2
Izod Impact, Notched (ISO)	5.50 kJ/m²	2.62 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	225 - 230 °C	437 - 446 °F
Vicat Softening Point	205 °C	401 °F	ISO 306
Heat Distortion Temperature	207 °C	405 °F	ISO 75-2
Flammability, UL94	HB	HB
Glow Wire Test	750 °C	1380 °F	60695-2-10

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	400 V	400 V	TS EN 60112

Processing Properties	Metric	English	Comments
Feed Temperature	70.0 °C	158 °F
Rear Barrel Temperature	220 - 250 °C	428 - 482 °F	Aft-1. Region Temperature
Middle Barrel Temperature	220 - 250 °C	428 - 482 °F	Mid-2. Region Temperature
Front Barrel Temperature	220 - 250 °C	428 - 482 °F	Pre-3. Region Temperature
Nozzle Temperature	225 °C	437 °F
Melt Temperature	220 - 230 °C	428 - 446 °F
Drying Temperature	110 - 120 °C	230 - 248 °F	Predrying Temperature
Dry Time	4 - 5 hour	4 - 5 hour	Predrying Time
Moisture Content	0.30 %	0.30 %	ISO 62

Descriptive Properties	Value	Comments
Block Temperature	80°C