Lehmann & Voss LUVOCOM® 1850/PL/15/BK PBT, with PTFE
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1850/PL/15/BK PBT, with PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Parts for electric and electronic industry.Coil formers, duty parts in plugs and switches, even combined with metal inserts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Water Absorption | <= 0.15 % | <= 0.15 % | 23°C/24h |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 45.0 MPa | 6530 psi | |
| Elongation at Yield | 10 % | 10 % | |
| 12 % | 12 % | flexural | |
| Modulus of Elasticity | 2.40 GPa | 348 ksi | |
| Flexural Strength | 80.0 MPa | 11600 psi | |
| Flexural Modulus | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.16 | 0.16 | |
| Coefficient of Friction, Static | 0.13 | 0.13 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
Vacuum Dryer |
| 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- SABIC MG500026 Linear Low Density Polyethylene for Compounding
- Polykemi AB SCANAMID 66 A53^EM Nylon 66, Modified
- Huntsman IROGRAN® CA116-203 TPU-Polyester
- Mallard Creek Polymers ROVENE® 4150 SBR Latex
- Teknor Apex Telcar® TL EF-6100 Thermoplastic Elastomer
- Chosun Refractories CSN-309N Plate Brick
- CIMBAR Miti-Wite B3 Chemically Purified White Barite (BaSO4)
- Dow Corning Z-6040® SILANE
- Colorite Polymers CS1542OR Wire and Cable Jacket Vinyl Compound
- Lehmann & Voss LUVOCOM® 1301-8212/BL PPS, linear, with glass fiber and PTFE
Copyright © lookpolymers.com All Rights Reserved