Total 5502 HDPE, blow molding, pipe
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | Total Atofina |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total 5502 HDPE, blow molding, pipe.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Drug Master File listed; USP Class VI approved; FDA compliant; UL 94HB/746 certified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | 50 hour | 50 hour | Condition B, 100% Igepal, F50; ASTM D1693 |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.35 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
| High Load Melt Index | 30 g/10 min @Load 21.6 kg, Temperature 190 °C |
30 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
| Tensile Impact Strength | 80.0 kJ/m² | 38.1 ft-lb/in² | Notched, -30°C; ISO 8256 |
| 185 kJ/m² | 88.0 ft-lb/in² | Notched, 23°C; ISO 8256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 129 °C | 264 °F | ASTM D3417 |
| Vicat Softening Point | 127 °C | 261 °F | ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Food Approval | This material complies with the main regulations concerning non-toxicity of plastics materials in contact with food stuffs. | |
| Process | Blow Molding | |
| Pipe Extrusion | ||
| Region | US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® ESD 7120
- Polykemi AB SCANAMID 66 A12^ F20 Nylon 66, Glass Fiber Reinforced
- DuPont Bynel® 3080 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin (discontinued **)
- Honeywell Capran® 518 LL Heat Stabilized Nylon Film (discontinued **)
- LG Chemical R320 EPS, Flame Retardant
- Monmouth Rubber & Plastics Durafoamâ„¢ C43NBR Nitrile Rubber
- Karina E 40/72-FC-LMP Green Color Concentrate for PVC
- A. Schulman POLYBATCH™ Blue 4012 Concentrate Based in Polyethylene
- Cossa Polimeri ESTABLEND 4500 Polycarbonate ABS Blend
- BASF Ultramid® A3Z HP BK20465 PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved