A. Schulman ComAlloy Voloy® 461 Glass Reinforced, PBT Alloy, Flame Retardant, UL
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Voloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Voloy® 461 Glass Reinforced, PBT Alloy, Flame Retardant, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 119 MPa | 17300 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 183 MPa | 26500 psi | ASTM D790 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.73 J/cm | 12.6 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 235 - 249 °C | 455 - 480 °F |
Users viewing this material also viewed the following:
- NeXolve CORIN XLS Polyimide
- Nilit FRIANYL B63 SG40 Nylon 6 for injection molding, 40% mineral filled
- SABIC Innovative Plastics Lexan® 3433R PC
- RheTech Products HP514-00 14% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- Spartech W17030LT-105 PVC and Alloy Products for Wire and Cable
- A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene
- 3M Scotchcal™ ElectroCut™ 7725-11 Graphic Film
- E-Polymers EFLEX® S1050 General
- DuPont™ Sclairfilm® SL-1 LLDPE Film, Laminating, 50.8 µm Thickness (discontinued **)
Copyright © lookpolymers.com All Rights Reserved