Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 9.00 kV/mm | 229 kV/in | |
Pyrotek TS-125 Thermoset Electrical Insulation Product Glass reinforcement, Polyester Resin, Brown Color. Very high mechanical strength at room and elevated temperature. Flame retardant.Information provided by Pyrotek. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | Step by Step; ASTM D149 |
Plenco 2424 Phenolic, Granular, Injection Molded
(discontinued **) Two-stage Phenolic. PLENCO 02424 is a black, two stage, general purpose phenolic molding compound. It has a good balance of properties for a general purpose type material. It is used in electrical .. |
|||
Dielectric Strength | 9.00 - 30.5 kV/mm | 229 - 775 kV/in | Average value: 28.2 kV/mm Grade Count:11 |
Overview of materials for Nylon 11, Powder This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11, Powder". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC 60 Hz |
Fujipoly Industries Sarcon® 30GHR Thin-Film GHR Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of .. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC 60 Hz |
Fujipoly Industries Sarcon® 30H Thin-Film HR Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of .. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC 60 Hz |
Fujipoly Industries Sarcon® 30U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | -40°C for 1,000 hrs; JIS-K-6249; ASTM D149 |
Fujipoly Industries Sarcon® NR-c Gap Filler Pad Non-Silicone Sarcon NR-c consists of an Acrylate resin and some thermal conductive fillers. It is a highly conformable/ thermally conductive material in a versatile sheet form that makes reliable and complete p.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149-95a |
Thermoseal KLINGERSIL® C-8200 Chemical Resistant Gasketing Synthetic FiberHypalon® BinderAcid ResistantGood Oil-Fuel ResistanceGood Gas SealabilityNo Color AddedInformation provided by Thermoseal Inc. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149 |
Tipco Tipcolite® TG 211 Phenolic Compound, Mineral & Wood Flour, Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149 |
Tipco Tipcolite® THD 111 Phenolic Compound, Short Glass Fibers & Minerals, Medium -Soft Flow & High Strength Medium -Soft Flow Phenolic Compound, Reinforced with Short Glass Fibres & MineralsApplications: Automotives & ElectricalProcessing: Compression & TransferInformation provided by the Manufacturer, T.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149 |
Tipco Tipcolite® THD 121 Phenolic Compound, Wood Flour, having Medium Flow & High Strength Medium Flow Phenolic Compound, Reinforced with Wood FlourApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India... |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149 |
Tipco Tipcolite® THR 211 Phenolic Compound, Asbestos Wood Flour & Minerals, Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Asbestos Wood Flour & MineralsApplications: Switchgear, HRC FusesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industrie.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149 |
Tipco Tipcolite® TX 211 Phenolic Compound, Wood Flour, having Medium Flow & High Electrical Properties Medium Flow Phenolic Compound, Reinforced with Wood FlourApplications: Switchgear, HRC FusesProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149 |
Tipco Tipcolite® TX 321 Phenolic Compound, Wood Flour & Minerals, having Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Wood Flour & MineralsApplications: Switchgear, HRC FusesProcessing: Injection MouldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
I.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ac; ASTM D116 |
CoorsTek Yttria Partially Stabilized Zirconia, YZTP, Sintered Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC; ASTM D116 |
CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | ac; ASTM D116 |
CoorsTek Zirconia-Toughened Alumina, ZTA Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC Rapid Rise; ASTM D149 |
DuPont™ Nomex® 411 Paper, 10 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC Rapid Rise; ASTM D149 |
DuPont™ Nomex® 411 Paper, 15 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC Rapid Rise; ASTM D149 |
DuPont™ Nomex® 411 Paper, 23 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC Rapid Rise; ASTM D149 |
DuPont™ Nomex® 411 Paper, 5 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC Rapid Rise; ASTM D149 |
DuPont™ Nomex® 411 Paper, 7 mil Nominal Thickness Nomex® Type 411 is the uncalendared precursor of Type 410. It has a lower density and lower property values. It is used in applications such as motor phase insulation and transformer coil end fil.. |
|||
Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC Rapid Rise; ASTM D149 |
DuPont™ Nomex® N196 Paper, 3 mil Nominal Thickness Nomex® Type N196 is a high floc grade of Nomex® paper. This leads to a high degree of saturability combined with high stiffness and mechanical properties. Type N196 is used where good saturabili.. |
|||
Dielectric Strength | 9.00 kV/mm @Thickness 0.400 mm |
229 kV/in @Thickness 0.0157 in |
thick |
Arkema Group Rilsan® Fine Powders Grey 49 Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p.. |
|||
Dielectric Strength | >= 9.00 kV/mm @Temperature 90.0 °C |
>= 229 kV/in @Temperature 194 °F |
IS 2584-1963 |
Amity Thermosets ATO 156 Phenolic Molding Glass Filler, Compression Molded Characteristics:High electrical insulationHigh mechanical strengthDimensional stabilityLow water absorptionColor-black Medium flow Applications: High electric insulation componentsHigh voltage swit.. |
|||
Dielectric Strength | >= 9.00 kV/mm @Temperature 90.0 °C |
>= 229 kV/in @Temperature 194 °F |
IS 2584-1963 |
Amity Thermosets ATO 159 Phenolic Molding Glass/ inorganic Filler, Compression Molded Characteristics:High electrical insulationHigh mechanical strengthDimensional stabilityLow water absorptionColor-black Medium flow Applications: High electric insulation componentsHigh voltage swit.. |