Material Notes:
Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 95
95
ASTM D2240
95
95
60°C for 500 hrs; ASTM D2240
96
96
150°C for 1,000 hrs; ASTM D2240
96
96
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 24.0 MPa
3480 psi
200°C for 1,000 hrs
26.6 MPa
3860 psi
ASTM D1458
31.67 MPa
4593 psi
150°C for 1,000 hrs; ASTM D1458
Elongation at Yield <= 2.0 %
<= 2.0 %
ASTM D1458
<= 2.0 %
<= 2.0 %
150°C for 1,000 hrs; ASTM D1458
<= 2.0 %
<= 2.0 %
200°C for 1,000 hrs; ASTM D1458
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 3.90e+9 ohm-cm
3.90e+9 ohm-cm
60°C for 500 hrs
1.00e+15 ohm-cm
1.00e+15 ohm-cm
3.90e+15 ohm-cm
3.90e+15 ohm-cm
150°C for 1,000 hrs
1.00e+16 ohm-cm
1.00e+16 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 3.1

@Frequency 50 Hz
 3.1

@Frequency 50 Hz
 After 1000 hrs at 150°C
3.1

@Frequency 1e+6 Hz
 3.1

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
3.1

@Frequency 1000 Hz
 3.1

@Frequency 1000 Hz
 After 1000 hrs at 150°C
3.5

@Frequency 1000 Hz
 3.5

@Frequency 1000 Hz
 After 1000 hrs at 200°C
3.5

@Frequency 1e+6 Hz
 3.5

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
3.5

@Frequency 50 Hz
 3.5

@Frequency 50 Hz
 After 1000 hrs at 200°C
3.9

@Frequency 50 Hz
 3.9

@Frequency 50 Hz
3.9

@Frequency 1000 Hz
 3.9

@Frequency 1000 Hz
3.9

@Frequency 1e+6 Hz
 3.9

@Frequency 1e+6 Hz
4.5

@Frequency 1e+6 Hz
 4.5

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
4.7

@Frequency 1000 Hz
 4.7

@Frequency 1000 Hz
 After 500 hrs at 60°C
5.0

@Frequency 50 Hz
 5.0

@Frequency 50 Hz
 After 500 hrs at 60°C
Dielectric Strength 5.70 kV/mm
145 kV/in
200°C for 1,000 hrs
7.00 kV/mm
178 kV/in
60°C for 500 hrs
7.00 kV/mm
178 kV/in
150°C for 1,000 hrs
9.00 kV/mm
229 kV/in
AC 60 Hz
Dielectric Breakdown 8000 V
8000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0010

@Frequency 1000 Hz
 0.0010

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 50 Hz
 0.0020

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 50 Hz
 0.0020

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0020

@Frequency 1000 Hz
 0.0020

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0030

@Frequency 1000 Hz
 0.0030

@Frequency 1000 Hz
0.0040

@Frequency 1e+6 Hz
 0.0040

@Frequency 1e+6 Hz
0.0040

@Frequency 1e+6 Hz
 0.0040

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0060

@Frequency 50 Hz
 0.0060

@Frequency 50 Hz
0.0080

@Frequency 1e+6 Hz
 0.0080

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
0.020

@Frequency 1000 Hz
 0.020

@Frequency 1000 Hz
 After 500 hrs at 60°C
0.069

@Frequency 50 Hz
 0.069

@Frequency 50 Hz
 After 500 hrs at 60°C
Descriptive Properties Value Comments
Color Brown
Thermal Impedance 0.61°C/W
FTM P-3010; ASTM D5470
Thermal Impedance AD Type 0.72°C/W
FTM P-3010; ASTM D5470