Fujipoly Industries Sarcon® 30U Thin-Film UR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 30U Thin-Film UR.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 79
79
ASTM D2240
85
85
60°C for 500 hrs with 95% RH; ASTM D2240
89
89
150°C for 1,000 hrs; ASTM D2240
92
92
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 3.00 MPa
435 psi
3.67 MPa
532 psi
60°C for 500 hrs with 95% RH
4.33 MPa
628 psi
150°C for 1,000 hrs
6.33 MPa
918 psi
200°C for 1,000 hrs
Elongation at Yield 40 %
40 %
150°C for 1,000 hrs
43 %
43 %
200°C for 1,000 hrs
73 %
73 %
60°C for 500 hrs with 95% RH
110 %
110 %
Tear Strength 0.300 kN/m
1.71 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 5.80e+13 ohm-cm
5.80e+13 ohm-cm
60°C for 500 hrs with 95% RH
1.00e+15 ohm-cm
1.00e+15 ohm-cm
2.00e+15 ohm-cm
2.00e+15 ohm-cm
200°C for 1,000 hrs
6.20e+15 ohm-cm
6.20e+15 ohm-cm
150°C for 1,000 hrs
Dielectric Constant 4.09

@Frequency 1000 Hz
 4.09

@Frequency 1000 Hz
 After 1000 hrs at 200°C
4.1

@Frequency 50 Hz
 4.1

@Frequency 50 Hz
 After 1000 hrs at 200°C
4.11

@Frequency 1e+6 Hz
 4.11

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
4.23

@Frequency 1000 Hz
 4.23

@Frequency 1000 Hz
 After 1000 hrs at 150°C
4.24

@Frequency 50 Hz
 4.24

@Frequency 50 Hz
 After 1000 hrs at 150°C
4.26

@Frequency 1e+6 Hz
 4.26

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
4.31

@Frequency 1000 Hz
 4.31

@Frequency 1000 Hz
4.32

@Frequency 50 Hz
 4.32

@Frequency 50 Hz
4.33

@Frequency 1e+6 Hz
 4.33

@Frequency 1e+6 Hz
4.34

@Frequency 1e+6 Hz
 4.34

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
4.38

@Frequency 1000 Hz
 4.38

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
4.45

@Frequency 50 Hz
 4.45

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Dielectric Strength 9.00 kV/mm
229 kV/in
AC 60 Hz
10.0 kV/mm
254 kV/in
150°C for 1,000 hrs
10.0 kV/mm
254 kV/in
200°C for 1,000 hrs
10.0 kV/mm
254 kV/in
60°C for 500 hrs with 95% RH
Dielectric Breakdown 6000 V
6000 V
Withstand Voltage [V/min]; AC 60 HZ
Dissipation Factor 0.00070

@Frequency 1e+6 Hz
 0.00070

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.00080

@Frequency 1000 Hz
 0.00080

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.00080

@Frequency 1000 Hz
 0.00080

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.00080

@Frequency 1e+6 Hz
 0.00080

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0011

@Frequency 1e+6 Hz
 0.0011

@Frequency 1e+6 Hz
0.0012

@Frequency 50 Hz
 0.0012

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0013

@Frequency 50 Hz
 0.0013

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0014

@Frequency 1000 Hz
 0.0014

@Frequency 1000 Hz
0.0027

@Frequency 50 Hz
 0.0027

@Frequency 50 Hz
0.0029

@Frequency 1e+6 Hz
 0.0029

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
0.0062

@Frequency 1000 Hz
 0.0062

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
0.0159

@Frequency 50 Hz
 0.0159

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Descriptive Properties Value Comments
Color Grey
Thermal Impedance 0.26°C/W
FTM P-3010; ASTM D5470