Amity Thermosets ATO 156 Phenolic Molding Glass Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATO 156 Phenolic Molding Glass Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:High electrical insulationHigh mechanical strengthDimensional stabilityLow water absorptionColor-black Medium flow Applications: High electric insulation componentsHigh voltage switch partsCross barsIron heat shieldCommutatorsVacuum cleaner partsAutomotive parts ( which ought to withstand thermal shocks )Wind Screen wiper partsWashing machine parts ( higher quality )Thermally and mechanically highly stressed partsInsulating flangesPulleysHigh quality castor wheelsPump housingElectric motor end shield , etc.Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.70 - 1.76 g/cc	0.0614 - 0.0636 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.750 - 0.850 g/cc	0.0271 - 0.0307 lb/in³	IS 867-1963
Water Absorption	0.15 - 0.20 %	0.15 - 0.20 %	IS 13411-1993
Linear Mold Shrinkage	0.0025 - 0.0040 cm/cm	0.0025 - 0.0040 in/in	IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	53.0 - 60.0 MPa	7690 - 8700 psi	5 mm/min.; IS 867-1963
Shear Strength	75.0 - 80.0 MPa	10900 - 11600 psi	IS 867-1963
Izod Impact, Notched	0.400 - 0.500 J/cm	0.749 - 0.937 ft-lb/in	IS 13411-1992

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.2e+11 - 3.2e+12 ohm-cm	3.2e+11 - 3.2e+12 ohm-cm	IS 3396-1979
Surface Resistance	1.00e+11 - 1.00e+12 ohm	1.00e+11 - 1.00e+12 ohm	IS 3396-1979
Dielectric Strength	>= 9.00 kV/mm @Temperature 90.0 °C	>= 229 kV/in @Temperature 194 °F	IS 2584-1963

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 180 °C	320 - 356 °F
Injection Pressure	15.68 - 34.3 MPa	2274 - 4970 psi	Mold Pressure
Cure Time	0.833 - 1.00 min	0.0139 - 0.0167 hour	per mm
Shelf Life	12.0 Month	12.0 Month	10-25°C

Users viewing this material also viewed the following: