CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped
| Category | Ceramic , Oxide , Zirconium Oxide |
| Manufacturer | CoorsTek |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a sharp decrease in the flexural strength of the sample.Data Provided by the manufacturer, CoorsTek, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 6.07 g/cc | 0.219 lb/in³ | ASTM C20 |
| Water Absorption | 0.00 % | 0.00 % | ASTM 373 |
| Particle Size | 1.0 µm | 1.0 µm | Thin Section Crystal Size |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Knoop Microhardness | 12.7 | 12.7 | 1000 g |
| Hardness, Rockwell 45 N | 81 | 81 | |
| Modulus of Elasticity | 210 GPa | 30500 ksi | ASTM C848 |
| Flexural Strength | 1720 MPa | 249000 psi | ASTM F417 |
| Compressive Strength | 2500 MPa | 363000 psi | ASTM C773 |
| Poissons Ratio | 0.23 | 0.23 | ASTM C848 |
| Fracture Toughness | 13.0 MPa-m½ | 11.8 ksi-in½ | Notched Beam |
| Shear Modulus | 85.0 GPa | 12300 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.3 µm/m-°C @Temperature 25.0 - 1000 °C |
5.72 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
| Specific Heat Capacity | 0.400 J/g-°C | 0.0956 BTU/lb-°F | ASTM E1269 |
| Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM C408 |
| Maximum Service Temperature, Air | 1500 °C | 2730 °F | No Load |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D1829 |
| <= 1000 ohm-cm @Temperature 1000 °C |
<= 1000 ohm-cm @Temperature 1830 °F |
ASTM D1829 | |
| 20000 ohm-cm @Temperature 500 °C |
20000 ohm-cm @Temperature 932 °F |
ASTM D1829 | |
| Dielectric Constant | 29 @Frequency 1e+6 Hz |
29 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC; ASTM D116 |
| Dissipation Factor | 0.0010 @Frequency 1e+6 Hz |
0.0010 @Frequency 1e+6 Hz |
ASTM D2520 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Ivory |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-30-20064 P Urethane Foam, Very Soft, Supported with Clear Polyester Film
- Karina 10/4040-IE White Color Concentrate MBU
- SIDPEC EGYPTENE® HD 5226 EA HDPE Injection Molding
- Samsung Cheil Industries Starex® GA-4025 ABS, 25% Glass Filled
- TPI Porene® GA300 High Flow Grade, High Gloss ABS
- Dow Corning SYL-OFF® 7210 RELEASE MODIFIER
- Covestro Bayblend® T90 MF-20* Polycarbonate + ABS, Mineral Filled
- Dow H700-12R Polypropylene Homopolymer Resin
Copyright © lookpolymers.com All Rights Reserved