SABIC Innovative Plastics LNP THERMOCOMP DF002 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF002 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF002 is a compound based on Polycarbonate resin containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
| 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| 81.0 MPa | 11700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 5.6 % | 5.6 % | Type I, 5 mm/min; ASTM D638 |
| 5.7 % | 5.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.8 % | 3.8 % | 5 mm/min; ISO 527 |
| 3.9 % | 3.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.17 GPa | 605 ksi | 1 mm/min; ISO 527 |
| 4.25 GPa | 616 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.95 GPa | 573 ksi | 2 mm/min; ISO 178 |
| 4.11 GPa | 596 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.810 J/cm | 1.52 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.83 J/cm | 16.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C @Thickness 3.20 mm |
295 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 30 LS Polyamide 6, 30% Glass Fiber, UV Stabilization
- PolyOne Geon™ Specialty Suspension CG E 44 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Kinlead HSS12 Normal Grade Heat Sealable Film (thickness: 18 µm)
- Indium Corp. Indalloy 26 Bismuth Solder Alloy
- SABIC Innovative Plastics Ultem 3451 PEI (Asia Pacific)
- Solvay Specialty Polymers Polidan® EC/MD Polyethylene, Crosslinked (XLPE)
- A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane
- 3M 2E98C Polyethylene Protective Tape
Copyright © lookpolymers.com All Rights Reserved