SABIC Innovative Plastics LNP STAT-KON DE004ER PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE004ER PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DE004ER is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added featuresof this material include: Electrically Conductive, Easy Molding, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00060 - 0.00090 cm/cm @Time 86400 sec |
0.00060 - 0.00090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | 5 mm/min; ISO 527 |
| 134 MPa | 19400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 133 MPa | 19300 psi | 5 mm/min; ISO 527 |
| 134 MPa | 19400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.88 GPa | 1868 ksi | 1 mm/min; ISO 527 |
| 14.86 GPa | 2155 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 197 MPa | 28600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 197 MPa | 28600 psi | ISO 178 | |
| Flexural Yield Strength | 197 MPa | 28600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.66 GPa | 1546 ksi | 2 mm/min; ISO 178 |
| 10.68 GPa | 1549 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.76 J/cm | 8.92 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 4.0 ohm | 2.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Synplast™ NOTM-E Tri (n-octyl) Trimellitate
- Pinnacle Polymers 1220 Polypropylene Homopolymer, Injection Molding Grade
- Michelman® Hydrosize® U1-01 Nonionic polyurethane dispersion
- Sibur MPP 15-06V Frost Resistant Polypropylene
- SABIC Innovative Plastics LNP Thermocomp WH0500B PBT
- Techmer ES HiFill FR® PA4/6 FR
- DuPont Performance Polymers Hytrel® 7246HS BK320 Polyester Elastomer TPC-ET (Unverified Data**)
- 3M FP082 Clear Polypropylene Label Products
- Materion Beryllium Copper Alloy 3 Tube; HT (TH04) Temper; up to 76 mm o.d. (UNS C17510)
Copyright © lookpolymers.com All Rights Reserved