SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.38 g/cc	0.0499 lb/in³	ASTM D792
	1.38 g/cc	0.0499 lb/in³	ISO 1183
Moisture Absorption	0.100 %	0.100 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0038 cm/cm @Time 86400 sec	0.0038 in/in @Time 24.0 hour	ISO 294
	0.0030 - 0.0050 cm/cm @Time 86400 sec	0.0030 - 0.0050 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ASTM D955
	0.0060 cm/cm @Time 86400 sec	0.0060 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	67.0 MPa	9720 psi	ASTM D638
	88.0 MPa	12800 psi	ISO 527
Tensile Strength, Yield	88.0 MPa	12800 psi	ASTM D638
	88.0 MPa	12800 psi	ISO 527
Elongation at Break	3.0 %	3.0 %	ISO 527
	3.5 %	3.5 %	ASTM D638
Elongation at Yield	2.9 %	2.9 %	ISO 527
	3.1 %	3.1 %	ASTM D638
Tensile Modulus	5.33 GPa	773 ksi	1 mm/min; ISO 527
	5.51 GPa	799 ksi	50 mm/min; ASTM D638
Flexural Strength	137 MPa	19900 psi	ASTM D790
	142 MPa	20600 psi	ISO 178
Flexural Modulus	4.82 GPa	699 ksi	ASTM D790
	5.10 GPa	740 ksi	ISO 178
Izod Impact, Notched	1.54 J/cm	2.89 ft-lb/in	ASTM D256
Izod Impact, Unnotched	7.58 J/cm	14.2 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	13.0 kJ/m²	6.19 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	44.0 kJ/m²	20.9 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	23.0 J	17.0 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	7.00 J	5.16 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.49	0.49	ASTM D3702 Modified
Coefficient of Friction, Static	0.54	0.54	ASTM D3702 Modified
K (wear) Factor	326 x 10^-8 mm³/N-M	162 x 10^-10 in³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	46.8 µm/m-°C @Temperature -40.0 - 40.0 °C	26.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	47.0 µm/m-°C @Temperature -40.0 - 40.0 °C	26.1 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	43.0 µm/m-°C @Temperature -40.0 - 40.0 °C	23.9 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
	43.2 µm/m-°C @Temperature -40.0 - 40.0 °C	24.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	145 °C	293 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	145 °C @Thickness 3.20 mm	293 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	141 °C	286 °F	Flatw 80104 sp=64mm; ISO 75/Af
	140 °C @Thickness 3.20 mm	284 °F @Thickness 0.126 in	unannealed; ASTM D648