Addiplast Addilene PMD 50272 Flame Retardant Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene PMD 50272 Flame Retardant Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, high rigidityInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183/A |
| Melt Flow | 16 g/10 min | 16 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | Conditioned; ISO 868 |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Conditioned; ISO R 527 |
| Elongation at Break | 4.0 % | 4.0 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 5.50 GPa | 798 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | ISO 75-2/AF |
| Vicat Softening Point | 162 °C | 324 °F | ISO 306/A50 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 850 °C | 1560 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Nyco HARRP™ 40 Wollastonite
- Lehmann & Voss LUVOCOM® 1105-7460/BL5019 PEEK, with glass fiber
- Lehmann & Voss LUVOCOM® 1301-8386 PPS, linear, with aramid reinforcement and PTFE
- LyondellBasell Alathon® M5352 High Density Polyethylene, Injection Molding Grade
- FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced
- A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
- Westlake Plastics Imidex Thermoplastic Polyimide
- Dow Corning SILASTIC® 9220/55 KIT PARTS A&B
- ArcelorMittal 07 High formability steel for drawing, Cold rolled
- SABIC Innovative Plastics Lexan® FXG154 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved