- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 460 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 460 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 6.35 mm |
460 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Therma-Tech™ NN-3000 TC Polyamide 66 (Nylon 66) Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Ovation Polymers Opnyl OP66GF15 Nylon 66, 14% Glass Reinforced Nylon 66 - Glass reinforced (14 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Oxford Polymers PPS/66-505-40GF-BK PPS/PA66, 40% Glass Fiber Reinforced Product Description: Glass Fiber (40% Reinforced), Polyphenylene sulfide injection molding grade based alloy with Nylon 66 Processing and Delivery Form: Pellets and Injection MoldingAppearance: Bla.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75, ASTM D648 |
| Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66 Description: Nilamid A3 H G3 ZB (13% Glass Reinforced) was developed for applications that require a combination of high stiffness and good elongation or impact resistance. It is widely used for app.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1013STHL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66 LNP* LUBRICOMP* RFL159 is a compound based on Nylon 66 resin containing 25% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant, Flame Retardant |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 LNP* LUBRICOMP* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific) LNP* Lubricomp* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY RF206XXH PA 66 LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing 40% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66 LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 20% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 238 °C | >= 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East) LNP* STAT-KON* RX98063 is a compound based on PA 66 resin containing Glass Fiber, Stainless Steel Fiber. Added features include; Antistatic. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 LGF50 HS L BK 12 mm Availability: North AmericaForms: PelletsFiller/Reinforcement: Long Glass FiberAdditive: Lubricant and Heat StabilizerFeatures: Lubricated, Heat Stabilized and Good MoldabilityUL File Number: E15731.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RFB24 is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1, 2 |
| Polyplastics FR-PET® B3030FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose Information provided by PolyPlastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Ashley Polymers Ashlene® 520-25G Nylon 66, 25% Glass Reinforced Nylon 66, 25% glass reinforced.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Resinoid 2016P Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||