Resinoid 2016P Phenolic Molding, Fabric Reinforced
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Fabric Filled |
| Manufacturer | Resinoid |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Resinoid 2016P Phenolic Molding, Fabric Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792A |
| Water Absorption | 0.80 % | 0.80 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 76 | 76 | ASTM D785 |
| Hardness, Rockwell M | 108 | 108 | ASTM D785 |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D651 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Compressive Strength | 159 MPa | 23100 psi | ASTM D695 |
| Izod Impact, Notched | 0.683 J/cm | 1.28 ft-lb/in | ASTM D256A |
| Charpy Impact, Notched | 0.683 J/cm² | 3.25 ft-lb/in² | J/cm; Notched; ASTM D256B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 9.60 kV/mm | 244 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 115 sec | 115 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 150 - 175 °C | 302 - 347 °F |
Users viewing this material also viewed the following:
- Network Polymers Softflex® 0150
- SABIC Innovative Plastics Lexan® ML6076 PC
- H.C. Starck HPM 1750 Tungsten High Density Composite Sheet
- Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK)
- A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy
- Tipco Tipcolite® TG 311 Phenolic Compound, Mineral & Wood Flour, Medium Flow & High Electrical Properties
- A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- ConocoPhillips Conoco® El Mar® Ashless Heavy Duty Oil, SAE Viscosity Grade 30
- ConocoPhillips Conoco® El Mar® Geo Low Ash Oil, SAE Viscosity Grade 30
Copyright © lookpolymers.com All Rights Reserved