SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
1.25 g/cc
0.0452 lb/in³
ASTM D792
Moisture Absorption 0.900 %
0.900 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.010 - 0.012 cm/cm

@Time 86400 sec
 0.010 - 0.012 in/in

@Time 24.0 hour
 ASTM D955
0.011 cm/cm

@Time 86400 sec
 0.011 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0079 cm/cm

@Time 86400 sec
 0.0079 in/in

@Time 24.0 hour
 ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
ISO 527
96.0 MPa
13900 psi
ASTM D638
Tensile Strength, Yield 95.0 MPa
13800 psi
ISO 527
96.0 MPa
13900 psi
ASTM D638
Elongation at Break 2.3 %
2.3 %
ISO 527
2.4 %
2.4 %
ASTM D638
Elongation at Yield 2.3 %
2.3 %
ISO 527
2.4 %
2.4 %
ASTM D638
Tensile Modulus 5.31 GPa
770 ksi
1 mm/min; ISO 527
5.51 GPa
799 ksi
50 mm/min; ASTM D638
Flexural Strength 149 MPa
21600 psi
ISO 178
Flexural Modulus 4.50 GPa
653 ksi
ISO 178
4.82 GPa
699 ksi
ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.21 J/cm
7.89 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 28.0 kJ/m²
13.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.46
0.46
ASTM D3702 Modified
Coefficient of Friction, Static 0.37
0.37
ASTM D3702 Modified
K (wear) Factor 318 x 10-8 mm³/N-M
158 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 42.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
43.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 24.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 73.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 252 °C
486 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
256 °C

@Thickness 3.20 mm
 493 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 221 °C
430 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
238 °C

@Thickness 3.20 mm
 460 °F

@Thickness 0.126 in
 unannealed; ASTM D648