SABIC Innovative Plastics LNP LUBRILOY RF206XXH PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY RF206XXH PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
1.24 g/cc
0.0448 lb/in³
ISO 1183
Moisture Absorption 0.350 %
0.350 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm

@Time 86400 sec
 0.0030 - 0.0040 in/in

@Time 24.0 hour
 ASTM D955
0.0032 - 0.0044 cm/cm

@Time 86400 sec
 0.0032 - 0.0044 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.011 - 0.012 cm/cm

@Time 86400 sec
 0.011 - 0.012 in/in

@Time 24.0 hour
 ASTM D955
0.0109 - 0.0124 cm/cm

@Time 86400 sec
 0.0109 - 0.0124 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 121 MPa
17500 psi
ISO 527
122 MPa
17700 psi
ASTM D638
Elongation at Break 2.6 %
2.6 %
ASTM D638
2.7 %
2.7 %
ISO 527
Tensile Modulus 8.20 GPa
1190 ksi
1 mm/min; ISO 527
8.89 GPa
1290 ksi
50 mm/min; ASTM D638
Flexural Strength 178 MPa
25800 psi
ASTM D790
192 MPa
27800 psi
ISO 178
Flexural Modulus 6.82 GPa
989 ksi
ASTM D790
8.50 GPa
1230 ksi
ISO 178
Izod Impact, Notched 1.22 J/cm
2.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.58 J/cm
14.2 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²
22.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 12.0 J
8.85 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.62
0.62
ASTM D3702 Modified
Coefficient of Friction, Static 0.43
0.43
ASTM D3702 Modified
K (wear) Factor 58.4 x 10-8 mm³/N-M
29.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
36.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 69.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
69.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 258 °C

@Thickness 3.20 mm
 496 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 238 °C
460 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
241 °C

@Thickness 3.20 mm
 466 °F

@Thickness 0.126 in
 unannealed; ASTM D648