SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RFB24 is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 147 MPa | 21300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.80 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 213 MPa | 30900 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 215 MPa | 31200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 101 µm/m-°C @Temperature 23.0 - 60.0 °C |
56.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PTS PCA-2201NHV Non Bromine, Non Chlorine Flame Retardant Polycarbonate/ABS Alloy, UV Stabilized
- Solvay Specialty Polymers Solef® 8808/0902 Carbon Fiber Reinforced PVDF Compound (discontinued **)
- SGL Carbon Group EK 2203 Carbon Graphite
- SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66
- A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene
- Dow Corning 7355 ADHESIVE
- Alliance S-30A Samarium Cobalt Magnetic Material
- Eastman Tenite Propionate 350E0096914 Natural, Trsp Cellulose Acetate Propionate
Copyright © lookpolymers.com All Rights Reserved