- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 275 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 275 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Plastcom SLOVASTER® B1 GF 10 PBT, 10% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 10% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D-648 |
| PlastiComp Complet® LCF50 - PP Homopolymer Polypropylene, 50% Long Carbon Fiber Reinforced Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polypropylene with 50% carbon fiber reinforcementInformation provided by PlastiComp, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | 120°C/h; ISO 75/1 |
| Polykemi AB SCANTEC PC S60R GF30 Polycarbonate, Glass-Fiber Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® BFL2010 PC (Asia Pacific) Non-brominated, non-chlorinated flame retardant, glass reinforced PC with improved flow. Available in opaque colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® EXL4019 PC (Asia Pacific) Lexan* EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers im.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 6.40 mm |
275 °F @Thickness 0.252 in |
ASTM D648 |
| PTS PPE-LXS 314-30 PPE-HIPS, 30% Glass Filled Typical Applications: Water industrial partsInformation provided by PTS LLC. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Kolon KOCETAL® TC702 Mineral Reinforced Acetal Resin Talc reinforced, improved dimensional stability. Applications: Products for high stiffness, dimensional precision. Information provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Isoflon PC Polycarbonate Good impact resistance among transparent materialsInformation provided by Isoflon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Fiberfil® J-61/10 Polypropylene Copolymer, 10% Glass Fiber Reinforced Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| LATI Latishield 87/28-10A PC, Steel Fiber Reinforced EMI shielding product based on Polycarbonate (PC). Steel fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplas.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DX05305C PC (Asia Pacific) LNP* Stat-kon* DX05305C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Samyang Trirex® 3025R Polycarbonate with Heat Stabilizer PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3025R is a general use grade with heat stabilizers and separating materials added.Appli.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DDF029 PC LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon, Glass Fiber. Added features of this material include: Electrically Conductive. Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS LNP* THERMOCOMP* NF004 is a compound based on PC+ABS resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL FE1520PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1520PW resin is a blend of polyphenylene oxide (PPO) and polystyrene (PS) resin that contains 20% glass reinforcement. The resin is suitable for injection molding. Noryl FE1520PW resin has .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS NORYL GFN1520V is a 20% glass fibre reinforced material with improved hydrolytic stability. This grade has been certified for potable water applications up to 85C in Europe and North America, color .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Washington Penn Homopolymer Polypropylene 20% Glass Reinforced Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ISO 75 |
| Polyram RamTough RZ300G2 Polycarbonate, 10% Glass Fiber 10% Glass fiber reinforced polycarbonate for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ISO 75 |
| Polyram RamTough RZ321G2 Polycarbonate, 10% Glass Fiber, Flame Retardant 10% Glass fiber reinforced, flame retardant polycarbonate for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | DIN EN ISO 75 |
| Wolf Kunststoff ZEDEX® ZX-530 A5D Polymer Alloy Main Characteristics: Low Creep; Low moisture absorption; Flame retardant; Low impurity ions; Good machinability; FDA compliant LABS; Extremely low outgassing; Less expensive than PEEK; Stress resis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | DIN 53461 |
| Polyram RamTough RZ309G18 Polycarbonate, 18% Glass Fiber 18% glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Covestro Makrolon® 8035 Polycarbonate High viscosity extrusion and injection molding grade with 30% short glass fibers and easy mold release, low anisotropy, for stiff moldings requiring good dimensional stability.Information provided b.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Clariant Renol PA223G13 Nylon 6, 13% Glass Fiber, Impact Modified Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Ashley Polymers Ashlene® RH190-PF Acetal, PTFE Filled A wear-resistant grade homopolymer resin with 1.5% PTFE.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS (Asia Pacific) NORYL GFN1520V is a 20% glass fibre reinforced material with improved hydrolytic stability. This grade has been certified for potable water applications up to 85C in Europe and North America, color .. |
|||