Samyang Trirex® 3025R Polycarbonate with Heat Stabilizer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3025R Polycarbonate with Heat Stabilizer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3025R is a general use grade with heat stabilizers and separating materials added.Applications: Microwave Oven Housing (light fastness)Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 68.6 MPa | 9960 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| Izod Impact, Notched | 7.85 J/cm @Thickness 3.17 mm |
14.7 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 - 70.0 µm/m-°C | 27.8 - 38.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.85 | 2.85 | ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dissipation Factor | 0.0092 | 0.0092 | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Carbon Fiber Reinforced
- Lord Adhesives Aeroglaze® M1433 Elastomeric Polyurethane Rain Erosion Coating
- Lubriplate 78 Cooker Oil Food Machinery Oil
- Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray)
- Sibur SKN-18SE Nitrile-Butadiene Rubber (NBR)
- Saint-Gobain Chemfab® 13 Anti-Static PTFE-Coated Glass
- A. Schulman POLYBATCH™ Green 3011E Concentrate Based In Polyethylene
- Arkema Group ORGASOL® 2002 D Nat 1 Polyamide 12, Food Contact Approved
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR Hi-Sil 243 LD Filler
- Arlon 44686W013 0.013" (0.330 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved