SABIC Innovative Plastics LNP THERMOCOMP WX93111 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP WX93111 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* WX93111 is a compound based on Polybutylene Terephalate resin containing Flame retardant , Glass Fiber, Proprietary filler. Added features include : Improved CTI.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
5 mm/min; ISO 527
Elongation at Break 0.60 %
0.60 %
5 mm/min; ISO 527
Tensile Modulus 8.90 GPa
1290 ksi
1 mm/min; ISO 527
Flexural Yield Strength 244 MPa
35400 psi
2 mm/min; ISO 178
Flexural Modulus 8.90 GPa
1290 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 34.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 18.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 77.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 42.8 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 UL 94 by SABIC-IP