Overview of materials for Phenolic, Novolac, Impact Grade, Filled

Category Polymer , Thermoset , Phenolic , Phenolic, Novolac, Impact Grade, Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Phenolic, Novolac, Impact Grade, Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Impact Grade, Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.34 - 1.70 g/cc
0.0484 - 0.0614 lb/in³
Average value: 1.41 g/cc Grade Count:21
Apparent Bulk Density 0.450 - 0.570 g/cc
0.0163 - 0.0206 lb/in³
Average value: 0.504 g/cc Grade Count:17
Water Absorption 0.300 - 1.00 %
0.300 - 1.00 %
Average value: 0.611 % Grade Count:19
Linear Mold Shrinkage 0.00350 - 0.0120 cm/cm
0.00350 - 0.0120 in/in
Average value: 0.00708 cm/cm Grade Count:21
Mechanical Properties Metric English Comments
Hardness, Rockwell E 85.0 - 90.0
85.0 - 90.0
Average value: 87.0 Grade Count:5
Tensile Strength, Ultimate 30.0 - 62.0 MPa
4350 - 8990 psi
Average value: 48.7 MPa Grade Count:21
Elongation at Break 0.200 - 0.840 %
0.200 - 0.840 %
Average value: 0.566 % Grade Count:5
Modulus of Elasticity 7.60 - 21.0 GPa
1100 - 3050 ksi
Average value: 11.1 GPa Grade Count:7
Flexural Yield Strength 62.0 - 94.0 MPa
8990 - 13600 psi
Average value: 75.7 MPa Grade Count:21
Flexural Modulus 6.70 - 19.0 GPa
972 - 2760 ksi
Average value: 8.15 GPa Grade Count:19
Compressive Yield Strength 100 - 234 MPa
14500 - 33900 psi
Average value: 200 MPa Grade Count:21
Izod Impact, Notched 0.240 - 0.290 J/cm
0.450 - 0.543 ft-lb/in
Average value: 0.259 J/cm Grade Count:15
Charpy Impact, Notched 0.100 - 0.286 J/cm²
0.476 - 1.36 ft-lb/in²
Average value: 0.223 J/cm² Grade Count:5
Thermal Properties Metric English Comments
CTE, linear 20.0 - 42.2 µm/m-°C
11.1 - 23.4 µin/in-°F
Average value: 33.6 µm/m-°C Grade Count:4
Maximum Service Temperature, Air 150 - 199 °C
302 - 390 °F
Average value: 178 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 135 - 206 °C
275 - 403 °F
Average value: 169 °C Grade Count:21
UL RTI, Electrical 150 °C
302 °F
Average value: 150 °C Grade Count:8
UL RTI, Mechanical with Impact 150 °C
302 °F
Average value: 150 °C Grade Count:8
UL RTI, Mechanical without Impact 150 °C
302 °F
Average value: 150 °C Grade Count:8
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:12
Electrical Properties Metric English Comments
Electrical Resistivity 6.00e+9 - 1.70e+14 ohm-cm
6.00e+9 - 1.70e+14 ohm-cm
Average value: 9.82e+12 ohm-cm Grade Count:19
Dielectric Constant 4.20 - 8.50
4.20 - 8.50
Average value: 5.79 Grade Count:17
Dielectric Strength 7.90 - 15.0 kV/mm
201 - 381 kV/in
Average value: 12.3 kV/mm Grade Count:19
Dissipation Factor 0.0360 - 0.240
0.0360 - 0.240
Average value: 0.0974 Grade Count:17
Arc Resistance 77.0 - 146 sec
77.0 - 146 sec
Average value: 121 sec Grade Count:3
Comparative Tracking Index 125 - 175 V
125 - 175 V
Average value: 146 V Grade Count:11