SABIC Innovative Plastics LNP STAT-KON KEL22A Acetal Homopolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON KEL22A Acetal Homopolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KEL22A is a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0033 cm/cm | 0.0033 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 7.9 % | 7.9 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| Elongation at Yield | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.40 GPa | 1220 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 82.0 MPa | 11900 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.10 GPa | 885 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 119 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® CY-1000 UV FR V0 Acrylonitrile Butadiene Styrene + PC (ABS+PC)
- SCG Chemicals EL-Proâ„¢ P702J Polypropylene Injection Molding
- Wellman Wellamid® NY1733-GY1 Lubricated, Nucleated, Unfilled Nylon 6
- Hexcel® HexWeb® HRH-327 - 3/16 - 4.5 Fiberglass Reinforced Polyimide Honeycomb
- CPC - Vycom FLAMETEC™ KYTEC® PVDF
- Dymax 9-20515 Peelable Mask
- 3D Systems Accura® accuGen™ HC and Ar Plastic for the SLA® 500 System
- Arlon T3030-R004 0.030" (0.762 mm) Thick, 1" wide, Cured Fusible Silicone Rubber with Sinusoidal Fiberglass Substrate
- 3M Cushion-Mount™ 1115 Plus Plate Mounting Tape
- Beijing Ranger Chem SM-604H Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved