| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | STN EN ISO 75/A |
| Plastcom SLOVALEN PH 51 T 40 Polypropylene Homopolymer, 40% Micronized Talc FeaturesModified homopolymer PP for injection moulding with the content of 40% micronized, floated, chemically modified talc. General application in all industry branches - packing material, garden.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | |
| Plastcom SLOVALEN PH 78 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. Stable towards detergents. General application in all industry branches.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
ASTM D648 |
| Ovation Polymers RIGITRON 10030 GF Polycarbonate, 30% Glass Reinforced PC - Glass reinforced (30 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® AD143 PC (Asia Pacific) LEXAN AD143 is a medium viscosity, injection molding grade exhibiting low dust attraction. It is designed for applications with high optical requirements in terms of clarity and light transmission .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® FXD951A PC Visual effetcs diffusion, flame retardant PC with low/medium flow good for extrusion/injection molding applications. Ideal for light management platforms that require hiding power and transmission.T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® PK2870 PC (Asia Pacific) LEXAN* PK2870 polycarbonate resin, global grade, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, blow molding, high melt strength, high impact resistance, Available in transparent colors onl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| Nilit FRIANYL B63 H-SG30 Nylon 6 for injection molding, 30% mineral filled Nylon 6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| Nilit FRIANYL B63 H-SG40 Nylon 6 for injection molding, 40% mineral filled Nylon 6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa JH820 Modified PC Features:Excellent balance propertiesSuper high impact strengthHigh stiffnessGood size stabilityGood surface, high glossHigh transparencyApplications:Injection moldingHousehold applianceBusiness mac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| GEHR Plastics PC Polycarbonate Polycarbonate shows a high rigidity and an extreme impact strength. Also it has a high glass transition temperature and temperature resistance. The operating temperature ranges from -60°C to appr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 19 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® 27 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® FC 19 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY EF1006F PC, Halogen Free, Flame Retardant, High Heat Resistance Description: Injection Molding, PC, Halogen Free Flame Retardant, High Heat ResistanceApplication: IT/OA Housing and Components (Adaptor)CAS: 103598-77-2Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Mitsubishi Xantar® FC 19 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL TN300 PPE+PS PPE+PS. Transparent. High heat. Color Limited. Injection molding. Laser-Transmission welding applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT LNP* LUBRICOMP* WAL34 is a compound based on (PBT resin containing 15% PTFE, 20% Aramid Fiber. Added features of this material include: Wesr Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP ZFL24 PPE+PS LNP* LUBRICOMP* ZFL24 is a compound based on PPE+PS resin containing 20% Glass Fiber, 10% PTFE. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Lubricomp ZFL24 PPO LNP* Lubricomp* ZFL24 is a compound based on Modified Polyphenylene Oxide (PPO) containing glass fiber and PTFE lubricant. Characteristics of this grade are: Internally Lubricated.This data was su.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DD0009E PC (Asia Pacific) LNP* Stat-kon* DD0009E is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp ML4351HF PC (Asia Pacific) LNP* Thermocomp* ML4351HF is a Light Reflecting Grade.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® HN-1064 PC, Unreinforced FR PC material that is applied to other resin for mobile phone chargersInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® VX4910 ASA+PBT (Europe-Africa-Middle East) 10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific) PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including wate.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | 120°C/hr; ASTM D 648 |
| Cossa Polimeri ESTAPROP KUR 1060 GFC Polypropylene, 30% Glass Filled PP copolymer 30% chemically coupled glass fiberElastomer modified, good impact strengthInformation provided by Cossa Polimeri S.r.l. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TR 55 PA12/MACMI Product description: Grilamid TR 55 natural is a high purity transparent thermoplastic polyamide, based on aliphatic and cycloaliphatic monomers. Grilamid TR 55 natural offers outstanding properties.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 |
| Asahi Kasei Xyron® A1400 PPE/PA Oil ResistantInformation provided by Asahi Kasei |
|||