Asahi Kasei Xyron® A1400 PPE/PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® A1400 PPE/PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Oil ResistantInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.900 % | 0.900 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.012 - 0.016 cm/cm | 0.012 - 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 140 % | 140 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 3.43 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
6.43 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | Resin Temperature |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | Pre-drying Temperature |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ PS-30CF/10T 2S Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced, PTFE/Silicone Lubricated
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 91A
- DSM Akulon® Ultraflow™ K-FG0 Nylon 6-50% Glass Reinforced (European and Asian Grade) (Dry) (discontinued **)&
- Kraton® D1161 E (SIS) Linear Triblock Copolymer
- Solvay Specialty Polymers Polidiemme® G/440 Thermoset Elastomer (TSE)
- EMS-Grivory Grivory® XE 4134 black 9225 PA*-GF30
- CLAL-MSX DECLAFOR® 1015 THX Rod quenched/Cold Rolled/Precipitation Heat Treated Copper Alloy
- Chosun Refractories CRAG-L38 Shroud Nozzle
- 3M 8437 Two-Sided Metalized
- 3M 5181 General Purpose PTFE Skived Film Tapes
Copyright © lookpolymers.com All Rights Reserved