SABIC Innovative Plastics NORYL TN300 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL TN300 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS. Transparent. High heat. Color Limited. Injection molding. Laser-Transmission welding applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Thickness 3.20 mm |
0.0070 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 31 g/10 min @Load 5.00 kg, Temperature 300 °C |
31 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 8.1 % | 8.1 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.73 GPa | 396 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.82 GPa | 409 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 161 °C | 322 °F | Rate B/50; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.581 | 1.581 | ASTM D542 |
| Haze | 7.3 % @Thickness 2.54 mm |
7.3 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 83.1 % | 83.1 % | 2.54 mm; ASTM D1003 |
Users viewing this material also viewed the following:
- Nylene® NX4528 Unfilled Nylon 6,6/6
- Huntsman Araldite ECN 1400 Water-Based Adhesive/Coating
- SABIC Innovative Plastics LNP STAT-KON DEL32P PC (Asia Pacific)
- Lubrizol Estane® X-585A-31 Thermoplastic Polyurethane
- DuPont Vamac® DP Sartomer 350 Coagent Test Compound
- Cossa Polimeri ESTAPROP K 0200 V2 Flame Retardant Polypropylene
- Chosun Refractories GUN-110L Light-Weight Gunning Castable
- Arkema Group KYNAR® 460 Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Copyright © lookpolymers.com All Rights Reserved