SABIC Innovative Plastics LNP Thermocomp ML4351HF PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp ML4351HF PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* ML4351HF is a Light Reflecting Grade.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D 792
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
 0.35 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 20 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 20 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D 1238
25 g/10 min

@Load 10.0 kg,
Temperature 260 °C
 25 g/10 min

@Load 22.0 lb,
Temperature 500 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 59.0 MPa
8560 psi
5 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 5 mm/min; ASTM D 638
55.0 MPa
7980 psi
5 mm/min; ISO 527
Elongation at Break 110 %
110 %
5 mm/min; ISO 527
130 %
130 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 5.0 %
5.0 %
Type I, 5 mm/min; ASTM D 638
5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 2.48 GPa
360 ksi
1 mm/min; ISO 527
2.55 GPa
370 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D 790
90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.25 GPa
326 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.46 GPa
357 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.80 J/cm

@Temperature -30.0 °C
 3.37 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
8.40 J/cm

@Temperature 23.0 °C
 15.7 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 25.0 kJ/m²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
60.0 kJ/m²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 60.0 J

@Temperature 23.0 °C
 44.3 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
130 °C

@Thickness 3.20 mm
 266 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 130 °C
266 °F
Rate B/50; ISO 306
131 °C
268 °F
Rate B/50; ASTM D 1525
132 °C
270 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C Passes
IEC 60695-10-2