Cossa Polimeri ESTAPROP KUR 1060 GFC Polypropylene, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP KUR 1060 GFC Polypropylene, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP copolymer 30% chemically coupled glass fiberElastomer modified, good impact strengthInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D 955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ASTM D 638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D 638 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ASTM D 638 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.30 J/cm @Temperature 0.000 °C |
2.44 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 1.70 J/cm @Temperature 23.0 °C |
3.18 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 120 °C @Load 5.00 kg |
248 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- Panipol Oy T Inherently Conductive Polymer
- FloMet 430L Stainless Steel
- Silikony Polskie Polsil OM 10000 Methyl Silicone Fluid
- Wellman Wellamid® GF33-66/6 XE-BK167A 33% Glass Filled, Color Matched Ebony Nylon 66/6
- Toyobo T-750 Nylon, Painting Grade
- A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene
- 3M 450EK Extended Liner Tapes
- Aclo Accutech Polypropylene Homopolymer HP0336T10L Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved