- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 210 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 210 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycolac® INP630 ABS+SAN INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance. Provides excellent hi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Asia Pacific) Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Polymer Resources PC/ABS-GP1-[color]-UV General Purpose PC/ABS Alloy, UV-stabilized PC/ABS Alloy, General Purpose, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provide.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Diameter 4.00 mm |
210 °F @Diameter 0.157 in |
Unannealed; bar; ISO 75-2 |
| NOVA Chemicals DYLARK® 378 Impact Grade Engineering Resin Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 - 146 °C | 210 - 295 °F | Average value: 108 °C Grade Count:22 |
| Overview of materials for Polycarbonate/ABS Alloy, NCG Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, NCG Fiber Filled". Each property range of values reported is minimum and maximu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| PolyOne Stat-Tech™ AS-15NCF/000 ABS - 15% Nickel Coated Carbon Fiber
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | |
| Ineos ABS Lustran® H702 Medium heat resistance, increased flow. ,Property data per ISO test methods. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| MRC Polymers NAXALOYâ„¢ 780 GF11 PC+PBT Polyester Blend, 11% Glass Fiber Filled Good chemical resistance, impact and heat resistanceAvailable in Black OnlyCan be UV StabilizedInternal and external lubricant can be added.Information provided by MRC Polymers Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KP004AH Acetal Homopolymer LNP* LUBRICOMP* KP004AH is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Asia Pacific) General purpose, UV stabilised Xylex gradeThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6 ML2 Nylon 6 Availability: North AmericaForms: PelletsAdditive: Molybdenum Disulfide Lubricant(2%)Features: Good Wear Resistance, Low Friction and LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO TS20 Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(20%) and Silicone LubricantFeatures: Lubricated, Good Wear Resistance and CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/ABS 1120 GF15 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedAppearance: Natural ColorInformation p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PC/ABS 1000 Availability: North AmericaForms: PelletsInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PC/ABS FR 1950 BK Availability: North AmericaForms: PelletsFeatures: Flame RetardantAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Annealed; ASTM Data |
| Styron Magnum™ SPD 214 ABS MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; 113°C (235°F) annealed; ASTM Data |
| Styron Pulse® 710 ABS + Polycarbonate PULSE® 710 Engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at both room and low temperatures. PULSE 710 Engineering resin h.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL N225X PPE+PS PPE+PS blend. Unfilled. Halogen-Free FR performance. UL94 V0/5VA. UL746C F1. Dielectric Strength. Suitable for E/E market indoor/outdoor applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Techmer ES Electrafil® J-1200/CF/10 ABS, 10% Carbon Fiber Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY NX03583 PC+ABS (Asia Pacific) LNP STAT-LOY* NX03583 is a compound based on PC+ABS Blend resin containing Anti-Static, Flame Retardant. Added features of this material include: Antistat. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO TL20 LE Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(20%) and Silicone LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction, Low Extractables and CopolymerUL File Number: E.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | |
| Zeon Chemicals Zeonor® 1060R Cyclo-Olefin Polymer Zeonor 1020R shall be in the form of pellets. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ISO 75-1,-2 |
| Covestro Bayblend® T50 BBS083 PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Injection molding• Goo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Asahi Kasei Thermofil D-10FG-1101 10% Glass Fiber Reinforced, ABS Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Ashley Polymers Ashlene® R190TB Acetal Impact modified reprocessed copolymer, excellent toughness, strength, stiffness and lubricity. Black.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Chase Plastics CP Pryme® PPH100-18M Polypropylene Homopolymer, 18 Melt Flow Information provided by Chase Plastics. |
|||