- Techmer ES Electrafil® J-1200/CF/10 ABS, 10% Carbon Fiber Reinforced
Techmer ES Electrafil® J-1200/CF/10 ABS, 10% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Electrafil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrafil® J-1200/CF/10 ABS, 10% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 1.87 J/cm @Thickness 3.17 mm |
3.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10.0 - 100 ohm-cm | 10.0 - 100 ohm-cm | ASTM C611 |
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V74E Fluoroelastomer Compound
- PTS Tristar® PC-10FR-(VIM) 12 MFI Flame Retardant, UV Stabilized Polycarbonate With Release
- Hardwire 3x2-4-12 Low Density Composite
- Solvay MIRACARE® P IS-C Surfactant
- Unifrax Fiberfrax® 7001-C-5 High Purity Bulk Fiber
- DuPont Elvax® 360 Ethylene-Vinyl Acetate Copolymer Resin
- Aclo Accutech Polypropylene Copolymer CP0437C40L Calcium Reinforced
- 3M Scotch® 250 Flatback Masking Tape
- Alliance BCNF-41 Bonded (Composite) Magnetic Material
- Park Electrochemical Nelco® N4000-6 FC Multifunctional Epoxy Laminate and Prepreg
Copyright © lookpolymers.com All Rights Reserved