- PolyOne Stat-Tech™ AS-15NCF/000 ABS - 15% Nickel Coated Carbon Fiber (discontinued **)
PolyOne Stat-Tech™ AS-15NCF/000 ABS - 15% Nickel Coated Carbon Fiber (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AS-15NCF/000 ABS - 15% Nickel Coated Carbon Fiber
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 0.12 % @Thickness 3.17 mm |
0.12 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 5.86 GPa | 850 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 10 ohm-cm | 1.0 - 10 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.0 - 10 ohm | 1.0 - 10 ohm | ASTM D257 |
| Shielding Effectiveness | 50 - 70 dB | 50 - 70 dB | 1,000 MHz; PolyOne Internal |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 232 °C | 400 - 450 °F | Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJKC304 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Termopol Termoton® V2GA0065A TPV Compound
- Gouda Vuurvast FI 25-15 Insulating Refractory Brick
- Karina 828-28/14-AY-ERYB Ice (Light Gray) PVC Compound
- Shandong Dongyue Shenzhou New Material Co DS603B Fluorinated Ethylene Propylene Dispersion (DS603A/B)
- Chevron Phillips Marlex® 1003 LDPE Injection Molding Resin
- BASF Ultramid® 8270 HS BK 102 PA6 (Dry)
- Asia International Enterprise (Hong Kong) 30G3F Polybutylene terephthalate, 15% Glass Fiber Filled
- Bulk Molding Compounds BMC 605LWR Mineral Filled, Glass Fiber Reinforced Polyester Compound