- HOME
- POLYMER SEARCH
- Thermoplastic
- ABS Polymer
- Acrylonitrile Butadiene Styrene (ABS), Molded
- Styron Magnumâ„¢ SPD 214 ABS
Styron Magnumâ„¢ SPD 214 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Styron |
| Trade Name | Magnum™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Magnumâ„¢ SPD 214 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming.MAGNUM® SPD 214 ABS resin is a low gloss, medium impact, blending/ coextrusion grade.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM Data |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 3.9 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.9 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | |
| Tensile Strength, Yield | 30.3 MPa | 4390 psi | ASTM Data |
| Elongation at Break | 50 % | 50 % | ASTM Data |
| Elongation at Yield | 1.8 % | 1.8 % | ISO Data |
| Tensile Modulus | 1.86 GPa | 270 ksi | ASTM Data |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM Data |
| Charpy Impact Unnotched | NB | NB | ISO Data |
| NB | NB | ISO Data, Low Temp | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO Data, Low Temp |
| 1.60 J/cm² | 7.61 ft-lb/in² | ISO Data |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature 20.0 °C |
46.7 µin/in-°F @Temperature 68.0 °F |
ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Annealed; ASTM Data |
| Vicat Softening Point | 104 °C | 219 °F |
Users viewing this material also viewed the following:
- Chevron Phillips Marlex® C513UV HDPE Blow Molding Resin (discontinued **)
- Sharadaa Ceramics HA 62 High Alumina Brick
- Shin-Etsu Silicones KSG-18 Fluid
- Samsung Cheil Industries Infino® HA-1011 PC/ABS, Unreinforced
- Eagle Brass 7026 Copper Nickel, 1/4 Hard
- Arlon CuClad 217 PTFE/Woven Fiberglass Laminate Microwave Printed Circuit Board Substrate
- BASF Elastollan® M85A55 Polyester Type Polyurethane Elastomer