- Asahi Kasei Thermofil D-10FG-1101 10% Glass Fiber Reinforced, ABS
Asahi Kasei Thermofil D-10FG-1101 10% Glass Fiber Reinforced, ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermofil |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermofil D-10FG-1101 10% Glass Fiber Reinforced, ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 3.93 GPa | 570 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.14 J/cm | 4.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 57.6 µm/m-°C @Temperature 20.0 °C |
32.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Flame Spread | 13 mm/min | 0.50 in/min | Horizontal Burn Rate; FMVSS302 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFlex™ GA-1042FR-60-0-405 Black TPE Compound
- Network Polymers Softflex® 0826
- Reade Advanced Materials Garnet Powder (Fe3Al2(SiO4)3)
- Fiberfil® J-60/40/E Polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled
- LG Chemical LUMID LW4403B(W) PA66+GF/MF40%, Low Warpage
- Indium Corp. Indalloy® 4 Pure Indium Solder
- Covestro Makrolon® 6585 Polycarbonate, Flame Retardant Grade
- CMT Materials HYTAC® C Castable Syntactic Tooling
- Arlon LW3015B##-P0 0.030" (0.762 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
Copyright © lookpolymers.com All Rights Reserved