SABIC Innovative Plastics LNP LUBRICOMP KP004AH Acetal Homopolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KP004AH Acetal Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KP004AH is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm @Time 86400 sec |
0.021 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0214 cm/cm @Time 86400 sec |
0.0214 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0205 cm/cm @Time 86400 sec |
0.0205 in/in @Time 24.0 hour |
ISO 294 |
| 0.021 cm/cm @Time 86400 sec |
0.021 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527 |
| 50.0 MPa | 7250 psi | ASTM D638 | |
| Elongation at Break | 10.5 % | 10.5 % | ISO 527 |
| 12.5 % | 12.5 % | ASTM D638 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | 50 mm/min; ASTM D638 |
| 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| 77.0 MPa | 11200 psi | ISO 178 | |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| 2.80 GPa | 406 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.16 | 0.16 | ASTM D3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Michelman® DigiGuard® Gloss 110 Overprint varnish
- Hannam Chemical Hanalac 775 ABS, Extrusion Grade
- MTM Plastics Dipolen® S Recycled PP + PE Blend
- SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI (Europe-Africa-Middle East)
- Teknor Apex APEX® 65005 Polyvinyl Chloride, Flexible
- A. Schulman PP 3471-01 Polypropylene High Flow Homopolymer Polypropylene
- 3M Scotch-Weld™ MG05 PR Medical Grade Instant Adhesive
- BASF Elastollan® 1160D Polyether Type Polyurethane Elastomer
- PolyOne Geon™ Vinyl Rigid Extrusion L6181 Polyvinyl Chloride, Rigid (PVC, Rigid)
Copyright © lookpolymers.com All Rights Reserved