SABIC Innovative Plastics NORYL N225X PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL N225X PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPE+PS blend. Unfilled. Halogen-Free FR performance. UL94 V0/5VA. UL746C F1. Dielectric Strength. Suitable for E/E market indoor/outdoor applications.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 17 %
17 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 8.0 %
8.0 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 99.0 MPa
14400 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 2.49 GPa
361 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 1.86 J/cm
3.48 ft-lb/in
ASTM D256
0.960 J/cm

@Temperature -30.0 °C
 1.80 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
8.86 J/cm

@Thickness 3.20 mm
 16.6 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Dart Drop, Total Energy 39.0 J
28.8 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
11.0 J

@Temperature -30.0 °C
 8.11 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 109 °C

@Thickness 6.40 mm
 228 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 99.0 °C

@Thickness 6.40 mm
 210 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 128 °C
262 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 95.0 °C
203 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 95.0 °C
203 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.400 mm
 HB

@Thickness 0.0157 in
 UL 94
V-0

@Thickness 1.47 mm
 V-0

@Thickness 0.0579 in
 UL 94
5VA

@Thickness 2.99 mm
 5VA

@Thickness 0.118 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.80e+16 ohm-cm
2.80e+16 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D257
Dielectric Constant 2.55

@Frequency 1.00e+6 Hz
 2.55

@Frequency 1.00e+6 Hz
 ASTM D150
2.69

@Frequency 50.0 - 60.0 Hz
 2.69

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Dielectric Strength 16.2 kV/mm

@Thickness 3.20 mm
 411 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
Dissipation Factor 0.0070

@Frequency 1.00e+6 Hz
 0.0070

@Frequency 1.00e+6 Hz
 ASTM D150
0.010

@Frequency 50.0 - 60.0 Hz
 0.010

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Radiant Panel Listing YES
UL Tested
UV-light, water exposure/immersion F1
UL 746C