- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 153 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 153 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Packaging PK8 WHITE 1081 Polyvinyl Chloride, Rigid (PVC, Rigid) The HDT value refers to samples conditioned @ 50 deg.C. for 24 hrs.The bulk density test was performed under ASTM D-1895B.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87556 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | STN EN ISO 75-2 (A) |
| Plastcom SLOVAMID 6 GB 30 HI PA6 reinforced with glass beads, improved impact strength PA 6 for injection molding, reinforced with 30% glass beads, impact modified. Application: impacted moldings and moldings with higher strength applied in automotive, electrical, engineering and cons.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 1.57 mm |
153 °F @Thickness 0.0618 in |
Annealed; ASTM D648 |
| PolyOne Novablend™ 5035 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.1 °C @Thickness 3.17 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| S&E Specialty Polymers TufFill™ 5000-SN4 PP, Flame Retardant Application: A No Bloom, UL 94 V-0 Polypropylene Compound TufFill™ 5000SN series is a specially engineered, low bloom, flame retardant polypropylene compound designed with halogen based technology... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC TS20020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC TS20020 UV Polypropylene Copolymer, Mineral Reinforced, UV-Stabilized Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPHC T8040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH K20020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ISO 75/Af |
| Solvay TECHNYL® B 216 Natural D PA66/6, DRY Description: Unreinforced copolyamide 66/6, medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL B 216 offers an excellent combination between impact resistance,.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RN001XXC PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RN001XXC is a compound based on Nylon 66 resin containing MOS2. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66 LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact, Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY KX09024 ACETAL COPOLYMER (Europe-Africa-Middle East) LNP* Statloy* KX09024 is a compound based on Polyacetal with reduced Resistivity. Added features include: Antistatic Properties |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C @Thickness 3.20 mm |
153 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP TF002 PU LNP* THERMOCOMP* TF002 is a compound based on Polyurethane resin containing 10% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Eastman Eastar DN001HF Copolyester Applications:DisplaysPersonal care and CosmeticsProduct Description: Eastar Copolyester DN001HF has excellent flow characteristics while maintaining superior mechanical properties. It is easy to p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Eastman Tenite 307A4000018 Propionate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Eastman Tenite 380A3V32818 Propionate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties if Tenite cellulosi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Eastman Tenite 572A1V95316 Cellulose Acetate Butyrate, Smoke, Trsp Applications:Molded partsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm fee.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Propionate 307A2R30018 Natural, Trsp Cellulose Acetate Propionate Plasticizer 18%. Weight loss on heating = 1% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Propionate 380A2R30018 Natural, Trsp Cellulose Acetate Propionate Plasticizer 18%. Weight loss on heating = 1% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Diamond Polymers SBS 1001 Styrene Butadiene Block Copolymer Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM D648 |
| Clariant Renol PBT1100 Black Polybutylene Terephthalate, General Purpose Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | |
| BASF Polystyrol® 473 D Impact Grade Polystyrene (Europe) Easy flowing, high-impact grade, often blended with easy flowing general purpose Polystyrol; easy to thermoform.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | |
| BASF Procom® D 1187 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM Test |
| BASF Styroclear GH 58 SBC Styroclear GH 58 is a high flow thermoplastic styrene-butadiene block copolymer with excellent mold release properties. It has crystal clarity, good toughness, good stiffness and warpage resistance.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPHC K8020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Lubrizol Stat-Rite® M-809 Static Control Acrylic Stat-Rite® M-809 is a static dissipative Acrylic alloy. Stat-Rite® M-809 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protec.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Eastman 9921W PET Injection Molded
(discontinued **) Voridian PET 9921W is a copolymer PET. Typical applications include containers for automotive parts, household products, and pharmaceutical and food packaging. Voridian PET thermoplastic polyesters .. |
|||