BASF Polystyrol® 473 D Impact Grade Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 473 D Impact Grade Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flowing, high-impact grade, often blended with easy flowing general purpose Polystyrol; easy to thermoform.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 200 °C |
12 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | |
| Elongation at Break | 35 % | 35 % | |
| Elongation at Yield | 1.2 % | 1.2 % | |
| Tensile Modulus | 1.70 GPa | 247 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 14.0 J/cm² @Temperature -30.0 °C |
66.6 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | |
| Vicat Softening Point | 80.0 °C | 176 °F | |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 425 V | 425 V |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_9610 Rubber-like Prototyping Polymer
- Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized
- Chevron Phillips HiD® 9606 HDPE Blown Film and Sheet (discontinued **)
- SABIC Innovative Plastics Lexan® HP4 PC
- Kennametal Stellite Stellite® 2006 Cobalt Alloy
- Indorama Ventures Mexico Polyclearâ„¢ T-94 PET Resin
- Iran Petrochemical (PCC) 09X02 Linear Low Density Polyethylene
- Johnson Matthey Mattibraze 45 Cadmium Containing Silver Brazing Alloy
- Diamond Polymers ABS TX-541
- Chosun Refractories BTN-2 Gas Purging Refractory
Copyright © lookpolymers.com All Rights Reserved