- Polykemi AB POLYfill PPHC T8040 Polypropylene, Mineral Reinforced
Polykemi AB POLYfill PPHC T8040 Polypropylene, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPHC T8040 Polypropylene, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Filler Content | 40 % | 40 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | With Flow; ISO 2577 |
| 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 27.0 MPa | <= 3920 psi | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 54.0 MPa | <= 7830 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 84.0 °C @Load 5.001 kg |
183 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 144 °C @Load 1.00 kg |
291 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- MV Labs TL400 TlCl Thallium(I) chloride
- Nanocyl NANOCYL™ NC2101 Double-Wall Isolated and Bundled Carbon Nanotubes - Research Grade
- Ovation Polymers Nemcon™ E PET 30131 PET
- Ravago Manufacturing Americas Hylon® N1043HL Nylon 6/6 (Cond)
- Plastcom SLOVASTER® B FRN 3 PBT, flame retarder
- Lucobit Lucowax® 1761 Polyethylene Wax
- DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 150 Gauge
- Cathay PA513 Renewable Engineering Polyamide
- BASF Neopolen® P 9035 0.07 g/cc Core density; Expanded Polypropylene (Europe)
- Axiall 5006 Rigid PVC, Extrusion, Natural
Copyright © lookpolymers.com All Rights Reserved