SABIC Innovative Plastics LNP THERMOCOMP TF002 PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TF002 PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* TF002 is a compound based on Polyurethane resin containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.610 % | 0.610 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.0 MPa | 5510 psi | Type I, 5 mm/min; ASTM D638 |
| 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | Type I, 5 mm/min; ASTM D638 |
| 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 53 % | 53 % | Type I, 5 mm/min; ASTM D638 |
| 55.4 % | 55.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 32.5 % | 32.5 % | Type I, 5 mm/min; ASTM D638 |
| 33.6 % | 33.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.26 GPa | 183 ksi | 1 mm/min; ISO 527 |
| 1.46 GPa | 212 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 26.0 MPa | 3770 psi | ISO 178 |
| Flexural Modulus | 0.900 GPa | 131 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 0.950 GPa | 138 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.34 J/cm | 6.26 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.3 J/cm | 23.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 129 kJ/m² | 61.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 29.0 J @Temperature 23.0 °C |
21.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 24.0 J | 17.7 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 89.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 172 µm/m-°C @Temperature -30.0 - 30.0 °C |
95.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 67.0 °C @Thickness 3.20 mm |
153 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 675A(IF) Synthetic Oil
- PolyOne Dynaflex™ G7640-9 (Black) Thermoplastic Elastomer (TPE)
- Resin Technology Group TIGA 108 Room Temperature Curing Epoxy Adhesive
- DuPont Performance Polymers Delrin® 100T BK602 Acetal Homopolymer (Unverified Data**)
- Lehmann & Voss LUVOCOM® 1800-8449 PET, with carbon fiber
- Momentive Performance Materials Addisilâ„¢ 1080 E Industrial Extrusion Heat Cured Rubber
- ExxonMobil 312 Mobilgard 12 Series
- ChevronTexaco ParaLux® 2401R Process Oil
- ExxonMobil LD 313.NF Blown Film Resin
- BASF Styropor® KF 462M EPS
Copyright © lookpolymers.com All Rights Reserved