SABIC Innovative Plastics LNP STAT-LOY KX09024 ACETAL COPOLYMER (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY KX09024 ACETAL COPOLYMER (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Statloy* KX09024 is a compound based on Polyacetal with reduced Resistivity. Added features include: Antistatic Properties
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.028 cm/cm | 0.028 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | 12 % | 12 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.00 GPa | 145 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 48.0 MPa | 6960 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 144 µm/m-°C @Temperature 23.0 - 60.0 °C |
80.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 159 µm/m-°C @Temperature 23.0 - 60.0 °C |
88.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 - 1.00e+10 ohm-cm | 1.00e+8 - 1.00e+10 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+8 - 1.00e+10 ohm | 1.00e+8 - 1.00e+10 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- MV Labs CU1000 CuSO4·5H2O Copper(II) sulfate pentahydrate
- Nitriflex NP-6121 Powdered Nitrile
- Parker Chomerics Tecknit Teckfip™ FIP-R Formed in Place Conductive Elastomer
- Sax Polymers SAXAMID 126F4 Nylon 6, 20% Glass Fiber
- Tipco Tipcolene® FPTC 30 HG - 30% Talc & Calcium Carbonate Polypropylene Homopolymer, High Gloss & Stiffness
- Polyplastics Duracon® SF-15 Acetal Co-polymer (POM), High impact, Flexible
- Zotefoams Plastazote® LD70 Low Density Polyethylene Foam
- Cytec (Conap) RN-1000 / EA-02 Conapoxy® Resin / Conacure® Hardener
- Eurostar Star L PA66 30V D51 PA66, Glass Fiber Filled, Injection Molded
- BASF Ultradur B 4300 G2 High Speed Unc. 10% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved