- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 74.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 74.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Nylene® PA6 Homopolymer 201 Nylon 6; Low Viscosity Nucleated Dry as molded.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC GF2007 PD1 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX7010 PC+ABS Cycoloy* CX7010 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0. Excellent flow combined with good balance of pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics GELOY CR3020 ASA Low-gloss ASA for profile and capstock applications |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Dry Blend E6530 Polyvinyl Chloride, Rigid (PVC, Rigid) Interior application for thick & thin gauge profile application.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Unannealed; ISO 75-2A |
| Total Lacqrene® 4240(EU) High Impact Polystyrene
(discontinued **) LACQRENE® 4240 is a high heat resistance, high impact polystyrene for the extrusion industry. Good mechanical and thermal properties leads to the production of thermoformed articles of good rigidi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Unannealed; ISO 75-2A |
| Total Lacqrene® 4241 High Impact Polystyrene
(discontinued **) DescriptionLACQRENE® 14240 is a high heat resistance, high impact polystyrene for the extrusion industry. Good mechanical and thermal properties leads to the production of thermoformed articles of.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| LATI LATAN 3E71 Polyoxymethylene Copolymer (POM) with Elastomer
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | |
| Eastman Tenite 105-33 Cellulose Acetate
(discontinued **) 33% Plasticized ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 - 216 °C | 165 - 420 °F | Average value: 96.5 °C Grade Count:13 |
| Overview of materials for Nylon 612 with PTFE Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612 with PTFE Filler". Each property range of values reported is minimum and maximum values of app.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | V-notch; ISO R 75 |
| Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate Application: friction bearings, wear linersInformation provided by Schwartz Technical Plastics GmbH |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP SG004 PA12 (Europe-Africa-Middle East) LNP* LUBRICOMP* SG004 is a compound based on PA 12 resin containing Graphite. Added features include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Supreme Petrochem SPEXP 44 Antistatic Polystyrene Characteristics Easy flow Good transparency Very good flexibility Processing Extrusion Applications Transparent profiles for electrostatic dissipative packaging of small electronic components such.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics NORYL FP3060 PPE+PS (Europe-Africa-Middle East) Noryl* FP3060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Eastman Tenite 550E3V45510 Cellulose Acetate Butyrate, Water Clear, Trsp Applications:AppliancesConsumer-Personal careProfilesProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Conditioned 4 hours @ 70°C (158°F); ASTM D648 |
| Eastman Tenite Butyrate 285A3720010 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 10%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® FG50 NC010 Nylon 66
(Unverified Data**) Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Unannealed; ASTM Data |
| Dow Retain® ABS 7342 ABS Data provided by Dow Chemical. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | unannealed; ISO 75 |
| Chi Mei Polylac® PA-765 ABS - Flame Retardant F.R. High Flow |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Adell EA-14 Homopolymer Polypropylene, 20% Talc Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Ashley Polymers Ashlene® 539L Nylon 66 High viscosity for injection molding of heavy parts.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM-D648 |
| Braskem Symbios 4102 Polypropylene Terpolymer Braskem Symbios 4102 is a medium melt flow rate terpolymer with a heat seal temperature below 120ºC on its treated face. It is designed for use as a heat sealing layer on bioriented films (BOPP) an.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Ashley Polymers Ashlene® 859 Nylon 6, Pellet form Ashlene 859 is offered in small pellet form. It is dried to less than 0.1% moisture eliminating the need for predrying. Ashlene 859 is molded with wall thickness ranging from 1/16" to greater than.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| A. Schulman ComAlloy Lubrilon® 640 Nylon 6/12, PTFE Reinforced, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||