SABIC Innovative Plastics NORYL FP3060 PPE+PS (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Noryl
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics NORYL FP3060 PPE+PS (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Noryl* FP3060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm and V0@ 2.5mm with a specific density of 1.1 g/cm^3. Noryl FP3060 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	ASTM D792
Density	1.10 g/cc	0.0397 lb/inÂ³	ISO 1183
Moisture Absorption	0.0200 %	0.0200 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	0.13 %	0.13 %	ISO 62
Melt Flow	42 g/10 min @Load 3.80 kg, Temperature 200 Â°C	42 g/10 min @Load 8.38 lb, Temperature 392 Â°F	ASTM D1238
Melt Index of Compound	20 g/10 min @Load 1.20 kg, Temperature 280 Â°C	20 g/10 min @Load 2.65 lb, Temperature 536 Â°F	MVR [cm^3/10 min]; ISO 1133
	41 g/10 min @Load 2.16 kg, Temperature 280 Â°C	41 g/10 min @Load 4.76 lb, Temperature 536 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield	54.0 MPa	7830 psi	Type I, 50 mm/min; ASTM D638
	55.0 MPa	7980 psi	50 mm/min; ISO 527
Elongation at Break	11 %	11 %	50 mm/min; ISO 527
	12 %	12 %	Type I, 50 mm/min; ASTM D638
Elongation at Yield	3.0 %	3.0 %	50 mm/min; ISO 527
	3.0 %	3.0 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.20 GPa	319 ksi	50 mm/min; ASTM D638
	2.42 GPa	351 ksi	1 mm/min; ISO 527
Flexural Yield Strength	82.0 MPa	11900 psi	2 mm/min; ISO 178
	84.0 MPa	12200 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.40 GPa	348 ksi	1.3 mm/min, 50 mm span; ASTM D790
	2.53 GPa	367 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.780 J/cm	1.46 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	6.00 kJ/mÂ²	2.86 ft-lb/inÂ²	80104; ISO 180/1A
	5.00 kJ/mÂ² @Temperature -30.0 Â°C	2.38 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	0.600 J/cmÂ²	2.86 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	83.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	46.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	83.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	46.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	80.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	44.4 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	80.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	44.4 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi)	74.0 Â°C	165 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	80.0 Â°C @Thickness 3.20 mm	176 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	91.0 Â°C	196 Â°F	Rate B/50; ISO 306
	93.0 Â°C	199 Â°F	Rate B/120; ISO 306
	105 Â°C	221 Â°F	Rate B/50; ASTM D1525
Flammability, UL94	V-1 @Thickness 1.50 mm	V-1 @Thickness 0.0591 in	UL 94 by SABIC-IP
	V-0 @Thickness 2.50 mm	V-0 @Thickness 0.0984 in	UL 94 by SABIC-IP