Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: friction bearings, wear linersInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | DIN 53473 |
| Water Absorption at Saturation | 0.60 % @Temperature 20.0 °C |
0.60 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 120 MPa | 17400 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO-DIS 527 |
| Creep Strength | 27.0 MPa | 3920 psi | 1% elongation, 1000 h; DIN 53444 |
| >= 45.0 MPa | >= 6530 psi | 2% elongation, 1000 h; DIN 53444 | |
| Flexural Strength | 125 MPa | 18100 psi | DIN 54352 |
| Flexural Modulus | 3.50 GPa | 508 ksi | DIN 53457 |
| Compressive Strength | 56.0 MPa | 8120 psi | 5% pressing; EN ISO 604 |
| 88.0 MPa | 12800 psi | 10% pressing; EN ISO 604 | |
| 95.0 MPa | 13800 psi | 20% pressing; EN ISO 604 | |
| Izod Impact, Notched (ISO) | >= 4.00 kJ/m² | >= 1.90 ft-lb/in² | DIN 53453 |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.020 - 0.080 | 0.020 - 0.080 | With lubrication |
| Coefficient of Friction, Dynamic | 0.24 - 0.28 | 0.24 - 0.28 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 0.50 | >= 0.50 | ISO-DIS 527 |
| K Factor (Wear Factor) | 1.5e-10 | 1.5e-10 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 - 100 °C |
44.4 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.05 J/g-°C | 0.251 BTU/lb-°F | |
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 255 °C | 491 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous |
| 180 °C | 356 °F | Intermittent | |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 5.00e+12 ohm | 5.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.6 | 3.6 | DIN 53483 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.019 | 0.019 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | Ka2 | DIN 53480 |
Users viewing this material also viewed the following:
- RheTech Products FRp256-01 Polypropylene Copolymer, Flame Retardant, Black
- Network Polymers NPP 808 C2WW
- SABIC Innovative Plastics Lexan® HFD1034 PC Copolymer (Europe-Africa-Middle East)
- Chevron Phillips HiD® 9075 HDPE Injection Molding Resin (discontinued **)
- Abatron AboCast 8-20/Abocure 8-20 Epoxy (discontinued **)
- Huntsman Araldite 94-105 Water-Based Hardener
- ICO Polymers ICOFLOâ„¢ 510-5051 800 Micron LDPE Powder
- Gwent Electronic Materials D2081009D6 Polymer Dielectric
- Synergy Polymers Ultra Purge HIGH-E
- A. Schulman POLYBATCH™ Yellow LL20212/4 Concentrate Based In LDPE
Copyright © lookpolymers.com All Rights Reserved