- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 254 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 254 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Unannealed; ISO 75-2/A |
| PolyOne OnForce™ LFT NN-60LGF/000 HS Natural Polyamide 66 (Nylon 66) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Owens Corning Glass Fiber Reinforced Nylon 6/6, 30 wt.% glass Nylons, as a group, are inert to most organic solvents. They resist alkalis and salt solutions and they are attacked by strong mineral acids and oxidizing agents. Data provided by the manufacturer,.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Quadrant EPP Techtron® PSGF PPS - Compression Molded 40% Glass Reinforced Polyphenylene Sulfide (ASTM Product Data Sheet) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1043L Nylon 6/6 (DAM) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66 LNP* Lubricomp* RFL16S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.This data was supplied by .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66 (Asia Pacific) LNP* Lubricomp* RFL16S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.This data was supplied by .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Techmer ES Electrafil® J-1/CF/20 Nylon 66, 20% Carbon Fiber Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF25 L BK 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 25% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF30 HS L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedProcessin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF33 HR HS BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabilized and Hydrolysis Resistant Appearance: .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF35 L UV 35% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Lubricated, Good UV Resi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF30 TL15 UV 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, UV Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resist.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF33 TS15 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear R.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Techmer ES Plaslube® J-1/30/TF/13/SI/2 NAT PA66 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Techmer ES Plaslube® J-1/30/TF/22 BK223 PA66 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF009H PA 66 LNP* THERMOCOMP* RF009H is a compound based on Nylon 66 resin containing 45% Glass Fiber. Added feature of this material is: Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF009H PA 66 (Asia Pacific) LNP* Thermocomp* RF009H is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RF00BS PA 66 (Asia Pacific) LNP* Thermocomp* RF00BS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ISO 75/Af |
| Solvay TECHNYL® A 218W V30 Natural PA66, 30% glass fiber, DRY Description: TECHNYL® A 218W V30 Nat is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. This product is available in natural color.Benefits: The produc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RC00A PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RC00A is a compound based on PA6.6 resin containing Carbon Fiber. Added features include: Electrically Conductive |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 - 257 °C | 490 - 495 °F | ASTM D648 |
| Clariant Renol PA1SP0019 Nylon 66/PPS Alloy, 20% Glass, 20% Mineral Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Clariant Renol PA111G33 Nylon 66, 33% Glass Fiber Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ASTM D-648 |
| PlastiComp Complet® LGF40 - PA66 Nylon 66, 40% Long Glass Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 40% long glass fiber reinforcementInformation provided by PlastiComp, In.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ASTM D-648 |
| PlastiComp Complet® LGF50 - PA66 Nylon 66, 50% Long Glass Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 50% long glass fiber reinforcementInformation provided by PlastiComp, In.. |
|||