Techmer ES Luriblend® PA6/6 GF33 TS15 33% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Heat Stabilized , Nylon 66, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 GF33 TS15 33% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Heat Stabilized and Low FrictionInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 148 MPa | 21400 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 222 MPa | 32200 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 | 0.20 | ASTM D1894 |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.596 MPa-m/sec | 17000 psi-ft/min | 10 fpm |
| 0.596 MPa-m/sec | 17000 psi-ft/min | 1000 fpm | |
| 0.666 MPa-m/sec | 19000 psi-ft/min | 100 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ NN-30GF/15T Black Polyamide 66 (Nylon 66)
- Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound (discontinued **)
- Ineos Styrenics Polystyrene 147F (NAFTA)
- Lehmann & Voss LUVOCOM® 1105-7781/BK PEEK, with carbon fiber
- Indium Corp. Indalloy 242 Tin-Lead Solder Alloy
- Inno-Comp INNOPOL® CS 1-1240 42% Chalk-Filled Polypropylene Homopolymer
- Eastman Tritan TX2000 Copolyester
- Diamond Polymers NPP25-1202 TF40 40% Talc Filled Copolymer Polypropylene
- Arlon 48B12R005 0.005" (0.127 mm) Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved