Techmer ES Electrafil® J-1/CF/20 Nylon 66, 20% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Electrafil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrafil® J-1/CF/20 Nylon 66, 20% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 67 | 67 | ASTM D785 |
| Tensile Strength, Ultimate | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 13.8 GPa | 2000 ksi | ASTM D638 |
| Flexural Yield Strength | 290 MPa | 42000 psi | ASTM D790 |
| Flexural Modulus | 15.2 GPa | 2200 ksi | ASTM D790 |
| Compressive Strength | 172 MPa | 25000 psi | ASTM D695 |
| Shear Strength | 82.7 MPa | 12000 psi | ASTM D732 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm |
1.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm @Thickness 3.17 mm |
10.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C |
10.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10.0 - 100 ohm-cm | 10.0 - 100 ohm-cm | ASTM C611 |
| Surface Resistance | 1000 - 10000 ohm | 1000 - 10000 ohm | ASTM D4496 |
Users viewing this material also viewed the following:
- LG Chemical Lutex 703 SBR Latex
- Kuraray SEPTON® A3 Hot Melt Adhesive
- SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene
- Tisan TISESTER® 30% Glass Fiber Reinforced Heat Stabilized Copolymer Polybutylene Terephthalate
- Covestro Baydur® GS PIR B Polyurethane
- Abatron AboGlass-1 Epoxy Decoupage Resin
- BASF Diethyleneglycol Divinyl Ether
- Huntsman Rexell® L8404 Cast Film Extrusion LLDPE (discontinued **)
- DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved