SABIC Innovative Plastics LNP THERMOCOMP RF00BS PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF00BS PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RF00BS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm @Time 86400 sec |
0.0029 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0044 cm/cm @Time 86400 sec |
0.0044 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 253 MPa | 36700 psi | ASTM D638 |
| 253 MPa | 36700 psi | ISO 527 | |
| Tensile Strength, Yield | 253 MPa | 36700 psi | ASTM D638 |
| 253 MPa | 36700 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 21.36 GPa | 3098 ksi | 1 mm/min; ISO 527 |
| 21.37 GPa | 3099 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 358 MPa | 51900 psi | ASTM D790 |
| 375 MPa | 54400 psi | ISO 178 | |
| Flexural Modulus | 19.3 GPa | 2800 ksi | ASTM D790 |
| 20.0 GPa | 2900 ksi | ISO 178 | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.28 J/cm | 23.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 76.0 kJ/m² | 36.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 38.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 16.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.89 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 16.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- DuPont Appeel® LSR 11D569 Modified EVA Lidding Sealing Resin (discontinued **)
- SABIC Innovative Plastics ULTEM SF2250 PEI Blend (Asia Pacific)
- SABIC Innovative Plastics NORYL GTX GTX989 PPE+PA (Europe-Africa-Middle East)
- Shin-Etsu Silicones KSG-830 Fluid
- Plenco 00714 Melamine-Phenolic, Granular, Injection Molded
- Zircar Ceramics Z-MAG/2300 Soluble Fiber Insulation
- Fainplast Compounds HAX HF 38 Halogen Free PVC
- Braskem PB681 LDPE Cast and Blown Film Extrusion, Injection Molding Polyethylene
- Murtfeldt Murylat® SP Polyethylene Terephthalate
Copyright © lookpolymers.com All Rights Reserved