SABIC Innovative Plastics LNP Lubricomp DFI12E PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp DFI12E PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFI12E is a compound based on Polycarbonate resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Easy Molding.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
1.27 g/cc
0.0459 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0049 cm/cm

@Time 86400 sec
0.0049 in/in

@Time 24.0 hour
ISO 294
0.0050 cm/cm

@Time 86400 sec
0.0050 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0057 cm/cm

@Time 86400 sec
0.0057 in/in

@Time 24.0 hour
ISO 294
0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 78.0 MPa
11300 psi
ASTM D 638
79.0 MPa
11500 psi
ISO 527
Tensile Strength, Yield 80.0 MPa
11600 psi
ASTM D 638
81.0 MPa
11700 psi
ISO 527
Elongation at Break 3.8 %
3.8 %
ISO 527
4.3 %
4.3 %
ASTM D 638
Elongation at Yield 3.4 %
3.4 %
ISO 527
3.5 %
3.5 %
ASTM D 638
Tensile Modulus 4.13 GPa
599 ksi
50 mm/min; ASTM D 638
4.21 GPa
611 ksi
1 mm/min; ISO 527
Flexural Strength 125 MPa
18100 psi
ISO 178
Flexural Modulus 4.00 GPa
580 ksi
ISO 178
4.13 GPa
599 ksi
ASTM D 790
Izod Impact, Notched 1.33 J/cm

@Temperature 23.0 °C
2.49 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 7.95 J/cm

@Temperature 23.0 °C
14.9 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 9.00 J
6.64 ft-lb
Multiaxial Impact; ISO 6603
5.00 J

@Temperature 23.0 °C
3.69 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 61.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
62.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
37.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 142 °C
288 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
136 °C

@Thickness 3.20 mm
277 °F

@Thickness 0.126 in
unannealed; ASTM D 648