Styron CALIBREâ„¢ 302V-6 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 302V-6 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 302V-6 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity (for tinted/transparent colors), and is available in both tinted/transparent and opaque colors. CALIBRE 302V-6 has a UV stabilizer.Govt. and Industry Standards: CSA (Canadian Standards Association)Underwriters Laboratory Inc. (UL) Applications:Electronic componentsAutomotiveLightingStorage Media HousingsInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A; ASTM D792 |
| Water Absorption | 0.25 % @Temperature 23.0 °C |
0.25 % @Temperature 73.4 °F |
Equilibrium, 50% RH; ISO 62; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4; ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 73 | 73 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
| 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | 3-point; ISO 178 |
| 96.5 MPa | 14000 psi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| Flexural Modulus | 2.41 GPa | 350 ksi | Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790 |
| Izod Impact, Notched | 9.10 J/cm @Temperature 23.0 °C |
17.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 88.0 kJ/m² @Temperature 23.0 °C |
41.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256; ISO 180 |
| Tensile Impact Strength | 588 kJ/m² | 280 ft-lb/in² | ASTM D1822 |
| Dart Drop, Total Energy | 90.4 J | 66.7 ft-lb | 3.39 m/sec; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Annealed; ISO 75-2/B; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Unannealed; ISO 75-2/B; ASTM D648 |
| 139 °C | 282 °F | Annealed; ISO 75-2/B; ASTM D648 | |
| Vicat Softening Point | 148 °C @Load 5.10 kg |
298 °F @Load 11.2 lb |
Rate A (50°C/h); ISO 306/B50; ASTM D1525 |
| Flammability, UL94 | 2.00 @Thickness 6.00 mm |
2.00 @Thickness 0.236 in |
White color |
| V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0626 in |
All color | |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
All color | |
| V-0 @Thickness 5.99 mm |
V-0 @Thickness 0.236 in |
Natural color, Black | |
| Oxygen Index | 26 % | 26 % | ISO 4289-2 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542; ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| 17.0 kV/mm | 432 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 Hz |
0.0010 @Frequency 50.0 Hz |
ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Average Extent of Burring | 3 cm | ASTM D635 |
Users viewing this material also viewed the following:
- Lanxess Durethan® DP 1441/40 H2.0 EF 900116 Nylon 6, 40% Glass Fiber + Mineral
- Techmer ES Elastoblend® PA6 IM 835 HS L
- SABIC Innovative Plastics LNP THERMOCOMP DX11354X PC (Asia Pacific)
- ExxonMobil Enmist EP 100
- Wellman Wellamid® GF33-66 XE-NBK1 33% Glass Fiber Reinforced, Engineering Grade Nylon 66
- Zeon Chemicals Nipol® 1051 Nitrile Elastomer
- Lubrizol Estane® 2103-85AE Thermoplastic Polyurethane Elastomer
- 3M 41826 Industrial Polyethylene Temporary Surface Protection Tape
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Iceberg Clay Filler
- Sumitomo Bakelite North America FS-6 CAF Mineral Filled Diallyl Phthalate
Copyright © lookpolymers.com All Rights Reserved