SABIC Innovative Plastics LNP LUBRILOY D2000 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY D2000 PC.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
Moisture Absorption 0.140 %
0.140 %
50% RH, 24 hrs; ASTM D570
0.180 %
0.180 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Time 86400 sec
 0.0080 in/in

@Time 24.0 hour
 ASTM D955
0.0084 cm/cm

@Time 86400 sec
 0.0084 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Time 86400 sec
 0.0080 in/in

@Time 24.0 hour
 ASTM D955
0.0081 cm/cm

@Time 86400 sec
 0.0081 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
Type I, 5 mm/min; ASTM D638
58.0 MPa
8410 psi
5 mm/min; ISO 527
Tensile Strength, Yield 57.0 MPa
8270 psi
Type I, 5 mm/min; ASTM D638
59.0 MPa
8560 psi
5 mm/min; ISO 527
Elongation at Break 47 %
47 %
Type I, 5 mm/min; ASTM D638
170 %
170 %
5 mm/min; ISO 527
Elongation at Yield 6.1 %
6.1 %
Type I, 5 mm/min; ASTM D638
6.6 %
6.6 %
5 mm/min; ISO 527
Tensile Modulus 2.05 GPa
297 ksi
5 mm/min; ASTM D638
2.09 GPa
303 ksi
1 mm/min; ISO 527
Flexural Strength 77.0 MPa
11200 psi
ISO 178
Flexural Modulus 1.97 GPa
286 ksi
2 mm/min; ISO 178
2.17 GPa
315 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.93 J/cm
13.0 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 59.0 kJ/m²
28.1 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
 36.9 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 42.0 J
31.0 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.16
0.16
ASTM D3702 Modified
Coefficient of Friction, Static 0.090
0.090
ASTM D3702 Modified
K (wear) Factor 121 x 10-8 mm³/N-M
60.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 41.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 76.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 42.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 139 °C
282 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
142 °C

@Thickness 3.20 mm
 288 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 128 °C
262 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
131 °C

@Thickness 3.20 mm
 268 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL 94